21-6-9 stainless aerospace tubing is a high manganese nitrogen strengthened, austenitic stainless steel with high strength in the annealed condition, excellent resistance to oxidation at high temperatures , good resistance to lead oxide and a high level of corrosion resistance at ambient temperatures. Applications include aircraft components, steam and autoclave parts, chemical and pollution control equipment.
| SKU |
Description |
OD |
Wall |
Specification |
| 46767 |
1/2 OD X .028 WALL |
0.5000 |
0.0280 |
AMS5561 |
| 46738 |
1/2 OD X .026 WALL |
0.5000 |
0.0260 |
AMS5561 BMS 7-185 |
| 71848 |
1 OD X .052 WALL |
1.0000 |
0.0520 |
AMS5561 BMS 7-185 |
Stock Size Range:
- OD: .188" - 3.00"
- Walls: .016" - .083"
- Tempers: Annealed
- Specifications: AMS 5561
| Typical Chemical Composition % |
| Weight % | Ni | Cr | Mn | C | Si | N | S | P |
|---|
| Minimum |
5.50 |
19.00 |
8.00 |
|
|
.15 |
|
|
|---|
| Maximum |
7.5 |
21.50 |
10.00 |
0.08 |
1.00 |
0.40 |
0.03 |
.06 |
|---|
| Typical Mechanical Properties |
| Ultimate | Yield | Elongation |
|---|
| KSI |
MPA |
KSI |
MPA |
% |
| 120 |
827 |
142-162 |
979-1117 |
20% |