Alloy C276 seamless nickel tubing is a nickel-molybdenum-chromium alloy with addition of tungsten having excellent corrosion resistance in a wide range of severe environments. The high molybdenum content makes this alloy especially resistant to pitting and crevice corrosion. The low carbon content minimizes carbide precipitation during welding to maintain corrosion resistance in as-welded structures.
Typical applications: pollution control, chemical processing, pulp and paper production, and waste treatment.
| SKU | Description | Manufacture Method | OD | Wall | Specification |
|---|---|---|---|---|---|
| 45439 | SMLS C-276 B622 .375 OD X .065 WA | SEAMLESS & DRAWN | 0.3750 | 0.0360 | ASME SB622 |
| 46394 | W HAST C-276 B626 3/8 X .035 WA | WELDED & DRAWN | 0.3750 | 0.0350 | ASTM B626 ASME SB626 |
| 46415 | SMLS HAST C-276 B622 1/2 X .049 WA | SEAMLESS & DRAWN | 0.5000 | 0.0490 | ASME SB622 |
| 46405 | SMLS C-276 B622 1/2 X .035 WA | SEAMLESS & DRAWN | 0.5000 | 0.0350 | ASME SB622 |
| 46376 | SMLS HAST C-276 B622 1/4 X .035 WA | SEAMLESS & DRAWN | 0.2500 | 0.0350 | ASME SB622 |
| Typical Chemical Composition % (max values, unless noted) | |||||||
|---|---|---|---|---|---|---|---|
| Nickel nominal | 57 | ||||||
| Chromium | 14.5-16.5 | ||||||
| Iron | 4.0-7.0 | ||||||
| Molybdenum | 15.0-17.0 | ||||||
| Cobalt | .5-2.5 | ||||||
| Sulfur | 0.03 | ||||||
| Tungsten | 3.0-4.5 | ||||||
| Cobalt | 2.5 | ||||||
| Carbon | 0.01 | ||||||
| Manganese | 1.0 | ||||||
| Silicon | 0.08 | ||||||
| Phosphorous | 0.04 | ||||||
| Vanadium | 0.35 | ||||||
| Typical Mechanical Properties | |||||
|---|---|---|---|---|---|
| Annealed | 1000 psi | Mpa | |||
| Yield Strength (0.2% offset) | 52 | 359 | |||
| Tensile Strength | 110.4 | 761 | |||
| Elongation % | 64 | ||||
| Rockwell Hardness | 83 B | ||||