Alloy 600 seamless nickel tubing is a nickel-chromium alloy with good oxidation resistance to 2000 degree F. Good strength and resistance to general corrosion in a variety of elements.
Resists stress-corrosion cracking.
Typical applications: thermocouple, furnace muffles, heat exchangers
| SKU | Description | Manufacture Method | OD | Wall | Specification |
|---|---|---|---|---|---|
| 46400 | SMLS ALLOY 600 B163 3/8 X .065 WA | SEAMLESS & DRAWN | 0.3750 | 0.0650 | ASTM B163 ASTM B167 |
| 46398 | SMLS ALLOY 600 B163 3/8 OD X .049 W | SEAMLESS & DRAWN | 0.3750 | 0.0490 | ASTM B163 ASTM B167 |
| 46392 | SMLS ALLOY 600 B163 3/8 OD X .035WA | SEAMLESS & DRAWN | 0.3750 | 0.0350 | ASTM B163 ASTM B167 |
| 46420 | SMLS ALLOY 600 B163 1/2 X .065 WA | SEAMLESS & DRAWN | 0.5000 | 0.0650 | ASTM B163 ASTM B167 |
| 46409 | SMLS ALLOY 600 B163 1/2 OD X.049 WA | SEAMLESS & DRAWN | 0.5000 | 0.0490 | ASTM B163 ASTM B167 |
| 46403 | SMLS ALLOY 600 B163 1/2 OD X.035 WA | SEAMLESS & DRAWN | 0.5000 | 0.0350 | ASTM B163 ASTM B167 |
| 46439 | SMLS ALLOY 600 B163 3/4 X .065 WA | SEAMLESS & DRAWN | 0.7500 | 0.0650 | ASTM B163 ASTM B167 |
| 46450 | SMLS ALLOY 600 B163 1 OD X .065 WA | SEAMLESS & DRAWN | 1.0000 | 0.0650 | ASTM B163 ASTM B167 |
| 46366 | SMLS ALLOY 600 B167 1/8 OD X .035WA | SEAMLESS & DRAWN | 0.1250 | 0.0350 | ASTM B163 ASTM B167 |
| 46381 | SMLS ALLOY 600 B163 1/4 OD X.049 WA | SEAMLESS & DRAWN | 0.2500 | 0.0490 | ASTM B163 ASTM B167 |
| Typical Chemical Composition % (max values, unless noted) | |||||||
|---|---|---|---|---|---|---|---|
| Nickel min. | 72.0 | ||||||
| Chromium | 14.9-17.0 | ||||||
| Iron | 6.0-10.0 | ||||||
| Copper | 0.5 | ||||||
| Sulfur | 0.015 | ||||||
| Carbon | 0.15 | ||||||
| Manganese | 1.0 | ||||||
| Silicone | 0.5 | ||||||
| Typical Mechanical Properties | |||||
|---|---|---|---|---|---|
| Annealed | Mpa | ||||
| Yield Strength (0.2% offset) psi | 35,000 min | 241 | |||
| Tensile Strength ksi min | 80,000 min | 552 | |||
| Elongation % in 2" | 30 | ||||